Mechanical property of Pyro-Carbon coated SiC fibers fabricated by continuous chemical vapor deposition method
Multidiscipline Modeling in Materials and Structures
ISSN: 1573-6105
Article publication date: 12 May 2022
Issue publication date: 16 June 2022
Abstract
Purpose
A continuous chemical vapor deposition (CVD) method has been used to fabricate pyro-carbon (PyC) coating on continuous silicon carbide (SiC) fibers. The paper aims to evaluate these coated fibers by testing filament tensile and using microstructure characterization.
Design/methodology/approach
The continuous SiC fiber-reinforced SiC matrix (SiC/SiC) composite is widely studied in aerospace and nuclear applications. The PyC is the probable option in fusion and fast reactor. However, the conventional fabrication method of PyC coating has some drawbacks influencing performance and efficiency.
Findings
The results showed that PyC-coated SiC fibers with continuous CVD method are more straight than conventional ones and residual deformations could not be observed, and these PyC coatings have complete geometry and uniform thickness. In different process conditions, the thickness of PyC coating could control from ∼100 to ∼1,000 nm.
Originality/value
The coated SiC fibers in a lower gas ratio (1:7 to 1:3), lower pressure (500–1,000 Pa) and appropriate winding speed (3 to 5 rpm) have relative high filament tensile strength (∼3.5 to ∼3.9 GPa). And the strength of coated SiC fibers has a negative correlation with the measured thickness of PyC coating. A distinctive growth process was discovered in the continuous CVD method. In a certain range, the quicker growing rate of PyC is obtained in shorter deposition time which means an efficient and quality method could be applied to fabricate coatings.
Keywords
Acknowledgements
This work was supported by the National Key R&D Program of China (No: 2018YFB1900603) and the Natural Science Foundation of Hunan Province (No: 2020JJ4667).
Citation
Li, C., Zhou, X., Gu, Q., Yan, X. and Wang, H. (2022), "Mechanical property of Pyro-Carbon coated SiC fibers fabricated by continuous chemical vapor deposition method", Multidiscipline Modeling in Materials and Structures, Vol. 18 No. 3, pp. 492-501. https://doi.org/10.1108/MMMS-03-2022-0041
Publisher
:Emerald Publishing Limited
Copyright © 2022, Emerald Publishing Limited