Preparation and properties of FeS/iron-based self-lubricating materials by chemical nickel plating-mechanical alloying

Abstract

Purpose

This paper aims to investigate the effect of chemical nickel plating and mechanical alloying on the mechanical and tribological properties of FeS/iron-based self-lubricating materials as well as the wear mechanism of the materials.

Design/methodology/approach

Surface modification of FeS powder was carried out by chemical nickel plating method and mechanical alloying of mixed powder by ball milling. The mechanical properties of the material were tested by tribological testing by M-200 ring block type friction and wear tester. Optical microscope was used to observe the surface morphology of the material and the transfer film on the surface of the mate parts, and scanning electron microscope and EDS were used to characterize the wear surface.

Findings

Mechanical alloying ball milling was carried out so that the lubricating particles in the matrix are uniformly dispersed; nickel-plated layer enhances the interfacial bonding of FeS and the matrix, and the combination of the two improves the mechanical properties of the material, and at the same time the friction side of the surface of the lubrication of FeS lubricant transfer film formed is denser and more intact, and the friction coefficient of friction side and the wear rate of the material have been greatly reduced.

Originality/value

This work aims to improve the mechanical and tribological properties of FeS/iron-based self-lubricating materials and to provide a reference for the preparation of materials with excellent overall properties.