Corrosion performance and morphological analysis of activated zinc phosphate coating formed on steel surface

Abstract

Purpose

The purpose of this paper is to study the effect of different concentrations of pretreatment solution of copper acetate (1, 5 and 10 g/L) on the deposition, growth and protection ability of zinc phosphate coating.

Design/methodology/approach

Zinc phosphate coatings were deposited on steel surface by immersion method. Scanning electron microscopy (SEM) and energy-dispersive spectroscopy (EDS) were used to study the morphological evolution and chemical analysis of formed coatings. The electrochemical performance of the coatings was evaluated via potentiodynamic polarization curves, electrochemical impedance spectroscopy (EIS) and immersion test in an aerated 3.5% NaCl solution.

Findings

The results showed that the activation treatment accelerated the deposition of the phosphate coating and improved its surface coverage. A higher phosphate coating weight (7.35 g/m²) and more compact structure was obtained with pretreatment solution of 1 g/L copper acetate. Electrochemical results revealed that the protection ability of the phosphated substrates was markedly enhanced after the pretreatment, and the best corrosion protection was obtained with a concentration of 1 g/L copper acetate solution. The corrosion current density of phosphated substrate was reduced by 64.9% after activation treatment with 1 g/L copper acetate solution.

Originality/value

In this investigation, dense, stable and compact zinc phosphate layers with improved corrosion resistance were formed on a carbon steel surface after activation pretreatment with copper acetate solution prior to a phosphating step.

Citation

Abdalla, K. and Zuhailawati, H. (2021), "Corrosion performance and morphological analysis of activated zinc phosphate coating formed on steel surface", Anti-Corrosion Methods and Materials, Vol. 68 No. 6, pp. 555-563. https://doi.org/10.1108/ACMM-03-2021-2462